Polymaker HT-PLA Green Filament 1.75mm 1Kg

Polymaker HT-PLA is a very easy-to-print high-temperature filament that provides reliable results for both beginners and professionals. It combines the user-friendliness of classic PLA materials with significantly increased heat resistance. Printed components remain stable up to 130°C, making the material suitable for applications subjected to high thermal stress. The excellent layer adhesion ensures precise printing results, while warping is minimized. HT-PLA also impresses with a high printing speed of up to 300 mm/s. Through optional annealing (approximately 30 minutes at 80–100 °C), the mechanical properties and temperature resistance can be significantly improved. Particularly noteworthy is the good paintability, as known from classic PLA: surfaces evenly absorb paints and lacquers, making the filament ideal for model making, tabletop miniatures, cosplay props, or custom interior car parts. This opens up possibilities with HT-PLA that would otherwise only be achievable with technical materials like ABS or ASA – but without their disadvantages such as limited color selection, complex processing, or higher printing requirements. Thus, HT-PLA combines the strengths of technical materials with the user-friendliness of PLA. During processing, there is a low odor development, slightly stronger than normal PLA, which is almost odorless, yet much more pleasant than ASA or ABS, which causes significantly more intense emissions.

Properties:

HT-PLA is heat-resistant and remains stable up to 130°C.
The material offers easy printability combined with high performance.
Layer adhesion is reliable and ensures precise results.
Warping occurs only to a small extent.
Low odor development, slightly stronger than PLA, but much more pleasant than ASA or ABS.
Optional annealing further improves properties.
Paintability as expected from PLA, ideal for model making, tabletop, and cosplay.
Offers the advantages of technical materials without the disadvantages in processing and color variety.

Recommended Printing Parameters:

Printing temperature: 210–230 °C, recommended 230 °C
Heated bed: 25–60 °C, recommended 50 °C
Fan: 100 %
Print speed: up to 300 mm/s

Documentation:

Technical Data:

Manufacturer: Polymaker
Manufacturer SKU: PA17006
Color: Green
Weight (net): 1 kg
Diameter: 1.75 mm
Tolerance: ±0.02 mm
Density: 1.287 g/cm³
Melt Flow Index: 22.6 g/10 min (210 °C/2.16 kg)
Tensile Strength (XY): 42.86 MPa
Tensile Strength (Z): 18.82–20.83 MPa
Elongation at Break (XY): 1.9–2.8 %
Elongation at Break (Z): 0.8–1.0 %
Flexural Strength (XY): 66.75–74.04 MPa
Flexural Strength (Z): 28.95–29.39 MPa
Flexural Modulus (XY): 2893–3267 MPa
Flexural Modulus (Z): 2411–2596 MPa
Impact Strength (Charpy XY): 4.7–4.9 kJ/m²
Impact Strength (Charpy Z): 4.4–4.5 kJ/m²
Heat Deflection Temperature (HDT 0.45 MPa): 156.2 °C (as printed), up to 155.2–156 °C (annealed)