Polymaker HT-PLA White Filament 1.75mm 1Kg

Polymaker HT-PLA is a very easy-to-print high-temperature filament that provides reliable results for both beginners and professionals. It combines the user-friendliness of traditional PLA materials with a significantly increased heat resistance. Printed parts remain dimensionally stable up to 130°C, making the material suitable for applications that need to withstand high thermal stress. The excellent layer adhesion ensures precise printing results, while warping is minimized. HT-PLA also impresses with a high printing speed of up to 300 mm/s. By optional annealing (about 30 minutes at 80–100 °C), the mechanical properties and temperature resistance can be further improved. Particularly noteworthy is the good paintability, as known from conventional PLA: surfaces evenly accept paints and coatings, making the filament ideal for model making, tabletop miniatures, cosplay props, or custom parts for vehicle interiors. Thus, HT-PLA opens up possibilities that were previously only achievable with technical materials like ABS or ASA – but without their disadvantages such as limited color selection, complex processing, or higher printing requirements. HT-PLA combines the strengths of technical materials with the user-friendliness of PLA. During processing, there is a low odor emission, slightly more than normal PLA, which is almost odorless, but far more pleasant than ASA or ABS, which cause significantly more intense emissions.

Features:

• HT-PLA is heat resistant and remains dimensionally stable up to 130°C.
• The material offers easy printability combined with high performance.
• The layer adhesion is reliable and ensures precise results.
• Warping occurs only to a minor extent.
• Low odor emission, slightly more than PLA, but much more pleasant than ASA or ABS.
• Optional annealing further improves properties.
• Paintability as expected from PLA, ideal for model making, tabletop, and cosplay.
• Offers the advantages of technical materials without their disadvantages in processing and color variety.

Recommended Printing Parameters:

• Printing temperature: 210–230 °C, recommended 230 °C
• Heated bed: 25–60 °C, recommended 50 °C
• Fan: 100%
• Printing speed: up to 300 mm/s

Documentation:

• Product Overview HT-PLA
• Datasheets HT-PLA

Technical Data:

• Manufacturer: Polymaker
• Manufacturer SKU: PA17002
• Color: White
• Weight (net): 1 kg
• Diameter: 1.75 mm
• Tolerance: ±0.02 mm
• Density: 1.287 g/cm³
• Melt Flow Index: 22.6 g/10 min (210 °C/2.16 kg)
• Tensile Strength (XY): 42.86 MPa
• Tensile Strength (Z): 18.82–20.83 MPa
• Elongation at Break (XY): 1.9–2.8%
• Elongation at Break (Z): 0.8–1.0%
• Bending Strength (XY): 66.75–74.04 MPa
• Bending Strength (Z): 28.95–29.39 MPa
• Bending Modulus (XY): 2893–3267 MPa
• Bending Modulus (Z): 2411–2596 MPa
• Impact Strength (Charpy XY): 4.7–4.9 kJ/m²
• Impact Strength (Charpy Z): 4.4–4.5 kJ/m²
• Heat Deflection Temperature (HDT 0.45 MPa): 156.2 °C (as printed), up to 155.2–156 °C (annealed)
• Spool Diameter (outer): 200 mm
• Spool Width: 65 mm
• Bore Diameter (inner): 55 mm
• Weight (gross): 1291 g
• Dimension: 205 x 225 x 75 mm