HT-PLA Gray Filament 1.75mm 1Kg R3D

The R3D HT-PLA Gray Filament is a high-temperature-resistant PLA filament with a diameter of 1.75 mm and a net weight of 1 kg. It features an increased Vicat softening temperature of 155.2 °C, making it significantly more heat-resistant than standard PLA. This material is particularly suitable for components exposed to higher temperatures. With a tensile strength of 40 MPa and a flexural modulus of 4106 MPa, the filament offers excellent mechanical properties for functional printed parts. The elongation at break is 11.8 %, indicating a balanced ratio between stiffness and flexibility. The filament is compatible with nozzle sizes from 0.2 to 0.8 mm and supports use in automatic material change systems (AMS). The impact strength is 4.2 kJ/m², while the interlayer adhesion is 2.7 kJ/m². For optimal print quality, the manufacturer recommends storing the filament in a cool, dry environment at 15 to 25 °C and protected from UV light. All spools are sealed and packaged with silica gel to minimize moisture absorption.

Recommended Accessories:

• 1 Liter Isopropyl Alcohol / Isopropanol 99.8%
• 3DLac Adhesion Spray 400ml
• Brass Wire Brush for Hotend / Nozzle Cleaning
• 3D Printer Accessory Kit

Properties:

• High-temperature resistance with a Vicat softening temperature of 155.2 °C enables use in warmer environments.
• Dimension tolerance of ±0.02 mm ensures a uniform and reliable material flow during printing.
• Compatibility with automatic material change systems (AMS) facilitates use in multi-filament setups.
• Flexural strength of 86 MPa provides high resistance to mechanical stress.
• Moisture absorption of only 0.4 % reduces sensitivity to environmental humidity.
• Nozzle compatibility from 0.2 to 0.8 mm allows flexible print resolutions for various requirements.

Recommended Printing Parameters:

• Nozzle temperature: 210–250 °C
• Bed temperature: 55–65 °C (adhesive recommended)
• Print speed: <300 mm/s
• Part cooling: 50–100 %
• Build chamber temperature: 25–45 °C
• Drying: 50–60 °C, 4–6 h

Application Examples:

• Functional prototypes that must withstand elevated temperatures
• Enclosures for electronics projects in warmer environments
• Mechanical parts with high flexural strength
• Mounts and fasteners for vehicle interiors
• Decorative objects with improved heat deflection resistance

Documentation:

• Data Sheet
• TigerTag RFID Connect App
• Manufacturer Website

Technical Data:

• Manufacturer: R3D
• Manufacturer SKU: R3DA1R105TMS
• Material: PLA High Temp (HT-PLA)
• Color: Gray
• Diameter: 1.75 mm
• Tolerance: ±0.02 mm
• Net weight: 1 kg
• Density: 1.22 g/cm³
• Melting temperature: 165 °C
• Vicat softening temperature: 155.2 °C
• Heat deflection temperature: 60.5 °C (ISO 75, 0.45 MPa)
• Tensile strength: 40 MPa
• Elongation at break: 11.8 %
• Flexural modulus: 4106 MPa
• Flexural strength: 86 MPa
• Impact strength: 4.2 kJ/m²
• Interlayer adhesion (Impact strength Z): 2.7 kJ/m²
• Moisture absorption: 0.4 % (23 °C, 50 % RH)
• Nozzle compatibility: 0.2–0.8 mm
• AMS-compatible: Yes
• Print bed compatibility: BuildTak, Glass, BlueTape, PEI
• Packaging dimensions: 210 × 210 × 70 mm
• Gross weight: 1420 g