HT-PLA Black Filament 1.75mm 1Kg R3D

The R3D HT-PLA Black filament is a high-temperature-resistant PLA filament with a diameter of 1.75 mm and a net weight of 1 kg. It features an increased Vicat softening temperature of 155.2 °C, making printed components significantly more heat-resistant than standard PLA. The melting temperature is 165 °C, and the heat deflection temperature is 60.5 °C at 0.45 MPa. The material offers a tensile strength of 40 MPa and a flexural modulus of 4106 MPa, indicating high stiffness and mechanical durability. The elongation at break is 11.8%, while the impact strength is 4.2 kJ/m². The adhesion between printed layers achieves an impact strength of 2.7 kJ/m² in the Z-direction. The filament is compatible with AMS systems and can be used with nozzle sizes from 0.2 to 0.8 mm. The spools are sealed and packed with silica gel to minimize moisture absorption. For optimal storage, the manufacturer recommends a cool, dry environment at 15 to 25 °C without UV exposure.

Recommended Accessories:

• 1 Liter Isopropyl Alcohol / Isopropanol 99.8%
• 3DLac Adhesion Spray 400ml
• Brass Wire Brush for Hotend / Nozzle Cleaning
• 3D Printer Accessories Kit

Properties:

• High-temperature resistance with a Vicat softening temperature of 155.2 °C enables components that are more resistant to heat than standard PLA.
• Tensile strength of 40 MPa and flexural modulus of 4106 MPa ensure high mechanical stability.
• Diameter tolerance of ± 0.02 mm guarantees a uniform material flow during printing.
• AMS compatibility allows use in automatic material change systems.
• Moisture absorption of only 0.4% reduces sensitivity to environmental humidity.
• Compatibility with nozzle sizes from 0.2 to 0.8 mm offers flexibility in choosing print resolution.

Recommended Printing Parameters:

• Nozzle temperature: 210–250 °C
• Bed temperature: 55–65 °C (adhesion promoter recommended)
• Print speed: < 300 mm/s
• Part cooling: 50–100%
• Build chamber temperature: 25–45 °C
• Drying: 50–60 °C, 4–6 h

Application Examples:

• Functional parts exposed to elevated temperatures, such as near electronic enclosures.
• Mechanical components with high stiffness for prototypes and fixtures.
• Mounts and covers in the interior of vehicles or machinery.
• Parts for the 3D printer itself, mounted near the heat bed or hotend.

Documentation:

• Data Sheet
• TigerTag RFID Connect App
• Manufacturer Website

Technical Data:

• Manufacturer: R3D
• Manufacturer SKU: R3DA1R106TMS
• Material: PLA High Temp (HT-PLA)
• Color: Black
• Diameter: 1.75 mm
• Diameter tolerance: ± 0.02 mm
• Net weight: 1 kg
• Density: 1.22 g/cm³
• Melt flow rate (MFR): 8 g/10 min (190 °C / 2.16 kg)
• Melting temperature: 165 °C
• Vicat softening temperature: 155.2 °C
• Heat deflection temperature: 60.5 °C (0.45 MPa)
• Tensile strength: 40 MPa
• Elongation at break: 11.8%
• Flexural modulus: 4106 MPa
• Flexural strength: 86 MPa
• Impact strength: 4.2 kJ/m²
• Layer adhesion (impact strength Z): 2.7 kJ/m²
• Moisture absorption: 0.4% (23 °C, 50% RH)
• AMS-compatible: Yes
• Nozzle compatibility: 0.2–0.8 mm
• Bed compatibility: BuildTak, Glass, BlueTape, PEI
• Packaging dimensions: 210 × 210 × 70 mm
• Gross weight: 1420 g