Polymaker HT-PLA-GF Power Tool Green Filament 1.75mm 1Kg

Polymaker HT-PLA-GF is a glass fiber-reinforced high-temperature filament that combines the easy printability of PLA with the high stability of technical compounds. Thanks to the glass fiber content, it offers exceptional rigidity, low shrinkage, and high dimensional stability. Components remain dimensionally stable up to 130°C after annealing, making it suitable for applications that are subjected to high mechanical and thermal loads. Despite the reinforcement, the material can be reliably printed and achieves print speeds of up to 350 mm/s. Particularly interesting is the good paintability as known from PLA: surfaces can be easily primed, painted, or dyed, making the filament ideal for model making as well as cosplay, tabletop, or custom vehicle parts. HT-PLA-GF thus opens up possibilities that would otherwise only be achievable with technical materials like ABS or ASA – but without their drawbacks such as limited color choices, complicated processing, or higher printing requirements. Due to the glass fiber reinforcement, the material is abrasive to nozzles, which is why the use of a hardened nozzle is expressly recommended. During processing, there is a slight odor development, stronger than with PLA, but significantly more pleasant than ASA or ABS.

Features:

• HT-PLA-GF offers high temperature resistance and remains dimensionally stable up to 130°C after annealing.
• Glass fiber reinforcement provides exceptional rigidity and stability.
• Very low shrinkage for precise and dimensionally accurate components.
• High layer adhesion and reliable printability.
• Low odor development, more pleasant than ASA or ABS.
• Paintability as expected from PLA, ideal for model making, tabletop, and cosplay.
• High print speed of up to 350 mm/s possible.
• Abrasive due to glass fiber – hardened nozzle recommended.

Recommended Printing Parameters:

• Print temperature: 210–230 °C, recommended 230 °C
• Heated bed: 25–60 °C, recommended 50 °C
• Fan: 100 %
• Print speed: up to 350 mm/s

Annealing: Place the finished part on a flat, heat-resistant surface and anneal at 100°C in the oven for about 30 minutes. Then slowly cool in the oven to avoid warping.

Documentation:

• Product Overview HT-PLA
• Data Sheets HT-PLA

Technical Data:

• Manufacturer: Polymaker
• Manufacturer SKU: PA18008
• Color: Power Tool Green
• Weight (net): 1 kg
• Diameter: 1.75 mm
• Tolerance: ±0.02 mm
• Density: 1.337 g/cm³
• Melt Flow Index: 22.9 g/10 min (210 °C/2.16 kg)
• Tensile Strength (XY): 50.2 MPa
• Tensile Strength (Z): 22.5–23.7 MPa
• Elongation at Break (XY): 2.3–2.8 %
• Elongation at Break (Z): 0.8–0.9 %
• Flexural Strength (XY): 86.4–87.8 MPa
• Flexural Strength (Z): 29.2 MPa
• Flexural Modulus (XY): 3685–4207 MPa
• Flexural Modulus (Z): 1954–2198 MPa
• Impact Toughness (Charpy XY): 4.9–5.3 kJ/m²
• Impact Toughness (Charpy Z): 4.3–4.4 kJ/m²
• Heat Deflection Temperature (HDT 0.45 MPa): 75.5 °C (as printed), 114.7 °C (annealed)
• Spool Diameter (outer): 200 mm
• Spool Width: 65 mm
• Hole Diameter (inner): 55 mm
• Weight (gross): 1266
• Dimension: 205 x 225 x 75mm

Included in Delivery:

• 1× Polymaker HT-PLA-GF Power Tool Green Filament 1.75mm 1Kg