HT-PLA Red Filament 1.75mm 1kg R3D

The R3D HT-PLA Red Filament is a high-temperature-resistant PLA filament with a diameter of 1.75 mm and a net weight of 1 kg. It features an increased Vicat softening temperature of 155.2 °C, making printed parts significantly more heat-resistant than standard PLA. The melting temperature is 165 °C, and the heat deflection temperature is 60.5 °C at 0.45 MPa. The material offers a tensile strength of 40 MPa and a flexural strength of 86 MPa, indicating good mechanical properties. The flexural modulus of 4106 MPa ensures high stiffness for printed parts. The elongation at break is 11.8 %, and the impact strength is 4.2 kJ/m². The filament is compatible with AMS systems and can be used with nozzle sizes from 0.2 to 0.8 mm. The manufacturing tolerance for the filament diameter is ±0.02 mm, ensuring uniform extrusion. All spools are sealed and packed with silica gel to prevent moisture absorption. For optimal storage, the manufacturer recommends a cool, dry environment at 15 to 25 °C without UV exposure.

Recommended Accessories:

• 1 Liter Isopropyl Alcohol / Isopropanol 99.8%
• 3DLac Adhesion Spray 400ml
• Brass Wire Brush for Hotend / Nozzle Cleaning
• 3D Printer Accessory Kit

Properties:

• High-temperature resistance with a Vicat softening temperature of 155.2 °C enables parts that are more heat-resistant than standard PLA.
• Manufacturing tolerance of ±0.02 mm ensures uniform and reliable extrusion.
• AMS compatibility allows use in automated material change systems.
• High flexural strength of 86 MPa and a flexural modulus of 4106 MPa ensure stiff and durable printed parts.
• Compatibility with nozzle sizes from 0.2 to 0.8 mm offers flexibility in print resolution.
• Moisture-protected packaging with silica gel ensures material quality until first use.

Recommended Printing Parameters:

• Nozzle temperature: 210–250 °C
• Bed temperature: 55–65 °C (adhesion promoter recommended)
• Print speed: <300 mm/s
• Part cooling: 50–100 %
• Build chamber temperature: 25–45 °C
• Drying: 50–60 °C, 4–6 h

Application Examples:

• Functional parts exposed to elevated temperatures, such as near electronic enclosures.
• Mechanical prototypes requiring high stiffness and dimensional accuracy.
• Components for use in vehicle interiors or sun-exposed environments.
• Mounts and assembly fixtures with enhanced heat resistance.

Documentation:

• Data Sheet
• TigerTag RFID Connect App
• Manufacturer Website

Technical Data:

• Manufacturer: R3D
• Manufacturer SKU: R3DA1R103TMS
• Material: PLA High Temp (HT-PLA)
• Filament diameter: 1.75 mm
• Tolerance: ±0.02 mm
• Color: Red
• Net weight: 1 kg
• Density: 1.22 g/cm³
• Melt Flow Rate (MFR): 8 g/10 min (190 °C / 2.16 kg)
• Melting temperature: 165 °C
• Vicat softening temperature: 155.2 °C
• Heat deflection temperature: 60.5 °C (0.45 MPa)
• Tensile strength: 40 MPa
• Elongation at break: 11.8 %
• Flexural modulus: 4106 MPa
• Flexural strength: 86 MPa
• Impact strength: 4.2 kJ/m²
• Impact strength Z-direction: 2.7 kJ/m²
• Moisture absorption: 0.4 % (23 °C, 50 % RH)
• Compatible nozzle sizes: 0.2–0.8 mm
• AMS-compatible: Yes
• Packaging dimensions: 210 × 210 × 70 mm
• Gross weight: 1420 g