Polymaker HT-PLA Orange Filament 1.75mm 1Kg

Polymaker HT-PLA is a very easy-to-print high-temperature filament that enables reliable results for both beginners and professionals. It combines the easy handling of classic PLA materials with significantly increased heat resistance. Printed parts remain stable up to 130°C, making the material suitable for applications that need to withstand high thermal loads. The excellent layer adhesion ensures precise printing results while warping is minimized. HT-PLA also impresses with high printing speed of up to 300 mm/s. Through optional annealing (approximately 30 minutes at 80–100 °C), the mechanical properties and temperature resistance can be significantly improved. Particularly noteworthy is the good paintability, as known from classic PLA: surfaces accept paints and varnishes evenly, making the filament ideal for model making, tabletop miniatures, cosplay props, or customized parts for vehicle interiors. This opens up possibilities with HT-PLA that would otherwise only be achievable with technical materials like ABS or ASA – but without their drawbacks like limited color choices, complex processing, or higher printing requirements. Thus, HT-PLA combines the strengths of technical materials with the user-friendliness of PLA. During processing, there is low odor development, slightly stronger than regular PLA, which is almost odorless, yet far more pleasant than ASA or ABS, which cause significantly more intense emissions.

Features:

HT-PLA is heat-resistant and remains stable up to 130°C.
The material offers easy printability combined with high performance.
The layer adhesion is reliable and ensures precise results.
Warping occurs only to a small extent.
Low odor development, slightly stronger than PLA, yet much more pleasant than ASA or ABS.
Optional annealing further enhances the properties.
Paintability as expected from PLA, ideal for model making, tabletop, and cosplay.
Offers the advantages of technical materials without their drawbacks in processing and color variety.

Recommended Printing Parameters:

Printing temperature: 210–230 °C, recommended 230 °C
Heated bed: 25–60 °C, recommended 50 °C
Fan: 100%
Printing speed: up to 300 mm/s

Documentation:

Technical Specifications:

Manufacturer: Polymaker
Manufacturer SKU: PA17009
Color: Orange
Weight (net): 1 kg
Diameter: 1.75 mm
Tolerance: ±0.02 mm
Density: 1.287 g/cm³
Melt Flow Index: 22.6 g/10 min (210 °C/2.16 kg)
Tensile Strength (XY): 42.86 MPa
Tensile Strength (Z): 18.82–20.83 MPa
Elongation at Break (XY): 1.9–2.8 %
Elongation at Break (Z): 0.8–1.0 %
Flexural Strength (XY): 66.75–74.04 MPa
Flexural Strength (Z): 28.95–29.39 MPa
Flexural Modulus (XY): 2893–3267 MPa
Flexural Modulus (Z): 2411–2596 MPa
Impact Toughness (Charpy XY): 4.7–4.9 kJ/m²
Impact Toughness (Charpy Z): 4.4–4.5 kJ/m²
Heat Deflection Temperature (HDT 0.45 MPa): 156.2 °C (as printed), up to 155.2–156 °C (annealed)
Spool Diameter Outer: 200 mm
Spool Width: 65 mm
Inner Hole Diameter: 55 mm
Weight (gross): 1291g
Dimension: 205 x 225 x 75mm