Polymaker HT-PLA White Filament 1.75mm 1Kg

Polymaker HT-PLA is a very easy-to-print high-temperature filament that provides reliable results for both beginners and professionals. It combines the user-friendliness of traditional PLA materials with a significantly increased heat resistance. Printed parts remain dimensionally stable up to 130°C, making the material suitable for applications that need to withstand high thermal stress. The excellent layer adhesion ensures precise printing results, while warping is minimized. HT-PLA also impresses with a high printing speed of up to 300 mm/s. By optional annealing (about 30 minutes at 80–100 °C), the mechanical properties and temperature resistance can be further improved. Particularly noteworthy is the good paintability, as known from conventional PLA: surfaces evenly accept paints and coatings, making the filament ideal for model making, tabletop miniatures, cosplay props, or custom parts for vehicle interiors. Thus, HT-PLA opens up possibilities that were previously only achievable with technical materials like ABS or ASA – but without their disadvantages such as limited color selection, complex processing, or higher printing requirements. HT-PLA combines the strengths of technical materials with the user-friendliness of PLA. During processing, there is a low odor emission, slightly more than normal PLA, which is almost odorless, but far more pleasant than ASA or ABS, which cause significantly more intense emissions.

Features:

HT-PLA is heat resistant and remains dimensionally stable up to 130°C.
The material offers easy printability combined with high performance.
The layer adhesion is reliable and ensures precise results.
Warping occurs only to a minor extent.
Low odor emission, slightly more than PLA, but much more pleasant than ASA or ABS.
Optional annealing further improves properties.
Paintability as expected from PLA, ideal for model making, tabletop, and cosplay.
Offers the advantages of technical materials without their disadvantages in processing and color variety.

Recommended Printing Parameters:

Printing temperature: 210–230 °C, recommended 230 °C
Heated bed: 25–60 °C, recommended 50 °C
Fan: 100%
Printing speed: up to 300 mm/s

Documentation:

Technical Data:

Manufacturer: Polymaker
Manufacturer SKU: PA17002
Color: White
Weight (net): 1 kg
Diameter: 1.75 mm
Tolerance: ±0.02 mm
Density: 1.287 g/cm³
Melt Flow Index: 22.6 g/10 min (210 °C/2.16 kg)
Tensile Strength (XY): 42.86 MPa
Tensile Strength (Z): 18.82–20.83 MPa
Elongation at Break (XY): 1.9–2.8%
Elongation at Break (Z): 0.8–1.0%
Bending Strength (XY): 66.75–74.04 MPa
Bending Strength (Z): 28.95–29.39 MPa
Bending Modulus (XY): 2893–3267 MPa
Bending Modulus (Z): 2411–2596 MPa
Impact Strength (Charpy XY): 4.7–4.9 kJ/m²
Impact Strength (Charpy Z): 4.4–4.5 kJ/m²
Heat Deflection Temperature (HDT 0.45 MPa): 156.2 °C (as printed), up to 155.2–156 °C (annealed)
Spool Diameter (outer): 200 mm
Spool Width: 65 mm
Bore Diameter (inner): 55 mm
Weight (gross): 1291 g
Dimension: 205 x 225 x 75 mm